Standard blank sizes for CNC machining (sheets & rods)
Tables of the standard blank sizes (sheets & rods) commonly used in CNC machining.
Introduction
The “blank” in CNC machining is the piece of material (metal or plastic) that is initially loaded to the machine. Stock materials come as plates (for CNC milling) or rods (for CNC turning) in a variety of sizes. In the tables below we summarize the most common blank dimensions found in a typical machine shop.
Note: 0.3 mm to 1.5 mm of material will be removed from each side of the blank during machining (that is up to 3 mm total). This should be taken into account during design as the blank size can significantly increase the material cost for large-scale productions.
Plates
Stock plates come pre-cut to size or as large sheet (typically, 2 m by 1 m - 6 ft. by 3 ft.) that are cut to blanks by the machine shop. So, the limiting dimension for a plate when it comes to design is its thickness.
The table below summarizes the most common aluminum and steel plate thicknesses that can be found in the warehouse of every machine shop. For an extensive, refer to a material supplier catalog.
| Thickness [mm] | Thickness [inches] |
|---|---|
| 3 mm | 3/16'' |
| 4 mm | 1/4'' |
| 5 mm | 5/16'' |
| 6 mm | 3/8'' |
| 8 mm | 7/16'' |
| 10 mm | 1/2'' |
| 12 mm | 5/8'' |
| 15 mm | 3/4'' |
| 20 mm | 1'' |
| 25 mm | 1/2'' increase therafter (up to 5'') |
| 30 mm | |
| 10 mm increase thereafter (up to 100 mm) |
Rods
Rods come as long stock (typically, 1 m - 3 ft. - or longer) that are cut to blanks by the machine shop. The limiting dimension here is the diameter of the rod.
The table below summarizes the most common aluminum and steel plate thicknesses that can be found in the warehouse of every machine shop. For an extensive, refer to a material supplier catalog.
| Diameter [mm] | Diameter [inches] |
|---|---|
| 3 mm | 1/8'' |
| 4 mm | 3/16'' |
| 5 mm | 1/4'' |
| 6 mm | 5/16'' |
| 7 mm | 3/8'' |
| 8 mm | 7/16'' |
| 9 mm | 1/2'' |
| 10 mm | 5/8'' |
| 12 mm | 3/4'' |
| 14 mm | 7/8'' |
| 15 mm | 1'' |
| 16 mm | 1/4'' increase therafter (up to 3'') |
| 20 mm | |
| 25 mm | |
| 30 mm | |
| 40 mm | |
| 10 mm increase therafter (up to 100 mm) |
More resources for engineers
Bevels: Machines and services for metal edge preparation
Read article
Counterbore versus countersink: key differences for engineers
Read article
Material ductility
Read article
Understanding shear stress and shear load
Read article
What is bulk modulus? Understanding material compression in engineering
Read article
What is subtractive manufacturing?
Read article
Understanding material stress vs. strain
Read article
What are countersinking holes and how do you use them?
Read article
Understanding tapped vs. rolled threads
Read article
Rz vs Ra roughness
Read article
Different types of quality documentation and when you need them
Read article
Tensile strength explained: definition and material performance
Tensile strength dictates the structural limits of your design. Learn how it impacts CNC machining, sheet metal forming, and 3D printing performance.
Read article
Bevels: Machines and services for metal edge preparation
Bevels explained: We help you to improve weld quality and structural integrity. Discover the best machines and get instant DfM feedback on your CAD.
Read article
Counterbore versus countersink: key differences for engineers
Counterbore versus countersink: These are the key differences for engineers. Read about the differences between these hole finishing methods.
Read article
Material ductility
Learn what ductility means, how it affects material deformation, and why it matters when selecting materials and designing reliable parts.
Read article
Understanding shear stress and shear load
Learn how shear stress affects your designs. Get practical formulas, material guidelines, and manufacturing tips to prevent shear failures in bolts, joints, and components.
Read article
What is bulk modulus? Understanding material compression in engineering
Bulk modulus measures material resistance to compression. Find out the formulas and why engineers use it for material selection in aerospace, automotive and more.
Read article
What is subtractive manufacturing?
Learn how subtractive manufacturing shapes parts by removing material. Explore CNC, drilling, laser cutting, and how it compares to additive methods.
Read article
Understanding material stress vs. strain
“Can you handle the pressure?” That’s the question engineers have to ask of every material they consider when they are designing for manufacturability. Stress and strain are fundamentals of material science, helping engineers assess how materials hold up under different forces. Read on to find out how they are measured.
Read article
What are countersinking holes and how do you use them?
Countersinking holes are conical holes designed to seat the head of a screw, bolt, or fastener so it sits flush with or just below the surface. This keeps the part’s outer layer smooth, which can improve its appearance, safety and performance. In this guide, we’ll drill into the ins and outs of countersinking, covering methods, applications, pros and cons, and tips for getting it just right.
Read article
Understanding tapped vs. rolled threads
What are tapped and rolled threads, and what do engineers need to know about them to manufacture high-performance parts? Find out here.
Read article
Rz vs Ra roughness
Rz and Ra are measurements used to describe and quantify surface roughness in manufacturing and engineering. Find out more about these different ways of measuring roughness as a machining finish for custom parts.
Read article
Different types of quality documentation and when you need them
Learn about the role quality documentation plays in the manufacturing process, how to obtain it, and the types of documentation that apply to parts, materials, and more
Read article